UL rated HB as of 10/97. 200 series recommended when V-2 rating required. Nonhalogenated. 10.5 MFR. UV-stabilized. Internal mold release.
TYPICAL PROPERTIES ¹
MECHANICAL
Tensile Stress, yld, Type I, 50 mm/minTensile Stress, brk, Type I, 50 mm/minTensile Strain, yld, Type I, 50 mm/minTensile Strain, brk, Type I, 50 mm/min
Flexural Stress, yld, 1.3 mm/min, 50 mm spanFlexural Modulus, 1.3 mm/min, 50 mm spanHardness, Rockwell MHardness, Rockwell R
Taber Abrasion, CS-17, 1 kg
TYPICAL VALUEUNITSTANDARD
626571109323407011810320480161691137132
6.84E-051.250.19130130
MPaMPa%%MPaMPa--mg/1000cyJ/mJ/mkJ/m²J°C°C°C1/°CJ/g-°CW/m-°C°C°C
ASTM D 638ASTM D 638ASTM D 638ASTM D 638ASTM D 790ASTM D 790ASTM D 785ASTM D 785ASTM D 1044ASTM D 4812ASTM D 256ASTM D 1822ASTM D 3029ASTM D 1525ASTM D 8ASTM D 8ASTM E 831ASTM C 351ASTM C 177UL 746BUL 746B
IMPACT
Izod Impact, unnotched, 23°C Izod Impact, notched, 23°CTensile Impact, Type \"S\"
Falling Dart Impact (D 3029), 23°C
THERMAL
Vicat Softening Temp, Rate B/50
HDT, 0.45 MPa, 6.4 mm, unannealedHDT, 1.82 MPa, 6.4 mm, unannealed CTE, -40°C to 95°C, flowSpecific Heat
Thermal Conductivity
Relative Temp Index, Elec
Relative Temp Index, Mech w/impact
1)Typical values only. Variations within normal tolerances are possible for variose colours.All values aremeasured at least after 48 hoursstorage at 230C/50% relative humidity.
All properties, expect the melt volume rate are measured on injectionmoulded samples.All samples are prepared according to ISO 294.
2)Only typical data for material selection purpose.Not to be used forpart or tool design.
3)This rating is not intended to reflect hazards presented this or anyother material under actual fire conditions.4)Own measurement according to UL.
Source, GMD, Last Update:04/14/2003
PLEASE CONTACT YOUR LOCAL SALES OFFICE FOR AVAILABILITY IN YOUR AREA DISCLAIMER : THE MATERIALS, PRODUCTS AND SERVICES OF SABIC INNOVATIVE PLASTICS HOLDING BV, ITS
SUBSIDIARIES AND AFFILIATES (\"SELLER\"), ARE SOLD SUBJECT TO SELLER'S STANDARD CONDITIONS OF SALE, WHICH CAN BE FOUND AT http://www.sabic-ip.com.AND ARE AVAILABLE UPON REQUEST.ALTHOUGH ANY INFORMATION OR RECOMMENDATION CONTAINED HEREIN IS GIVEN IN GOOD FAITH, SELLER MAKES NO WARRANTY OR GUARANTEE, EXPRESS OR IMPLIED, (i) THAT THE RESULTSDESCRIBED HEREIN WILL BE OBTAINED UNDER END-USE CONDITIONS, OR (ii) AS TO THE EFFECTIVENESS OR SAFETY OF ANY DESIGN INCORPORATING SELLER'S PRODUCTS,SERVICES OR
RECOMMENDATIONS. EXCEPT AS PROVIDED IN SELLER'S STANDARD CONDITIONS OF SALE, SELLER SHALL NOT BE RESPONSIBLE FOR ANY LOSS RESULTING FROM ANY USE OF ITS PRODUCTS ORSERVICES DESCRIBED HEREIN.Each user is responsible for making its own determination as to the suitability of Seller's products, services or recommendations for the user's particular use through appropriate end-use testingand analysis. Nothing in any document or oral statement shall be deemed to alter or waive any provision of Seller's Standard Conditions of Sale or this Disclaimer,unless it is specifically agreed to in a writing signed Seller. Nostatement Seller concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right of Seller or as a recommendation for theuse of such product, service or design in a manner that infringes any patent or other intellectual property right.* Lexan is a trademark of SABIC INNOVATIVE PLASTICS HOLDING BV© 1997-2008 SABIC INNOVATIVE PLASTICS HOLDING BV.All rights reserved
Lexan* Resin 143R
Americas: COMMERCIAL
TYPICAL PROPERTIES ¹
THERMAL
Relative Temp Index, Mech w/o impact
1301.20.831.190.150.350.580.5 - 0.710.58811.586>1.E+1714.93.172.960.00090.0142120.76
°C-m³/gc
g/cm³%%%%
g/10 min%%-Ohm-cmkV/mm----PLC CodePLC CodePLC CodePLC Codemm
UL 746BASTM D 792ASTM D 792ASTM D 792ASTM D 570ASTM D 570ASTM D 570SABIC MethodASTM D 1238ASTM D 1003ASTM D 1003ASTM D 2ASTM D 257ASTM D 149ASTM D 150ASTM D 150ASTM D 150ASTM D 150UL 746AUL 746AUL 746AUL 746AUL 94
TYPICAL VALUEUNITSTANDARD
PHYSICAL
Specific GravitySpecific VolumeDensity
Water Absorption, 24 hours
Water Absorption, equilibrium, 23C Water Absorption, equilibrium, 100°CMold Shrinkage, flow, 3.2 mm Melt Flow Rate, 300°C/1.2 kgf
OPTICAL
Light TransmissionHaze
Refractive Index
ELECTRICAL
Volume Resistivity
Dielectric Strength, in air, 3.2 mmRelative Permittivity, 50/60 HzRelative Permittivity, 1 MHzDissipation Factor, 50/60 HzDissipation Factor, 1 MHzHot Wire Ignition {PLC)
High Voltage Arc Track Rate {PLC}High Ampere Arc Ign, surface {PLC}Comparative Tracking Index (UL) {PLC}
FLAME CHARACTERISTICS
UL Recognized, 94HB Flame Class Rating (3)
1)Typical values only. Variations within normal tolerances are possible for variose colours.All values aremeasured at least after 48 hoursstorage at 230C/50% relative humidity.
All properties, expect the melt volume rate are measured on injectionmoulded samples.All samples are prepared according to ISO 294.
2)Only typical data for material selection purpose.Not to be used forpart or tool design.
3)This rating is not intended to reflect hazards presented this or anyother material under actual fire conditions.4)Own measurement according to UL.
Source, GMD, Last Update:04/14/2003
PLEASE CONTACT YOUR LOCAL SALES OFFICE FOR AVAILABILITY IN YOUR AREA DISCLAIMER : THE MATERIALS, PRODUCTS AND SERVICES OF SABIC INNOVATIVE PLASTICS HOLDING BV, ITS
SUBSIDIARIES AND AFFILIATES (\"SELLER\"), ARE SOLD SUBJECT TO SELLER'S STANDARD CONDITIONS OF SALE, WHICH CAN BE FOUND AT http://www.sabic-ip.com.AND ARE AVAILABLE UPON REQUEST.ALTHOUGH ANY INFORMATION OR RECOMMENDATION CONTAINED HEREIN IS GIVEN IN GOOD FAITH, SELLER MAKES NO WARRANTY OR GUARANTEE, EXPRESS OR IMPLIED, (i) THAT THE RESULTSDESCRIBED HEREIN WILL BE OBTAINED UNDER END-USE CONDITIONS, OR (ii) AS TO THE EFFECTIVENESS OR SAFETY OF ANY DESIGN INCORPORATING SELLER'S PRODUCTS,SERVICES OR
RECOMMENDATIONS. EXCEPT AS PROVIDED IN SELLER'S STANDARD CONDITIONS OF SALE, SELLER SHALL NOT BE RESPONSIBLE FOR ANY LOSS RESULTING FROM ANY USE OF ITS PRODUCTS ORSERVICES DESCRIBED HEREIN.Each user is responsible for making its own determination as to the suitability of Seller's products, services or recommendations for the user's particular use through appropriate end-use testingand analysis. Nothing in any document or oral statement shall be deemed to alter or waive any provision of Seller's Standard Conditions of Sale or this Disclaimer,unless it is specifically agreed to in a writing signed Seller. Nostatement Seller concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right of Seller or as a recommendation for theuse of such product, service or design in a manner that infringes any patent or other intellectual property right.* Lexan is a trademark of SABIC Innovative Plastics IP BV© 1997-2008 SABIC Innovative Plastics IP BV.All rights reserved
Lexan* Resin 143R
Americas: COMMERCIAL
TYPICAL PROPERTIES ¹
FLAME CHARACTERISTICS
Oxygen Index (LOI)
UV-light, water exposure/immersion
25F1
%-ASTM D 2863
UL 746C
TYPICAL VALUEUNITSTANDARD
1)Typical values only. Variations within normal tolerances are possible for variose colours.All values aremeasured at least after 48 hoursstorage at 230C/50% relative humidity.
All properties, expect the melt volume rate are measured on injectionmoulded samples.All samples are prepared according to ISO 294.
2)Only typical data for material selection purpose.Not to be used forpart or tool design.
3)This rating is not intended to reflect hazards presented this or anyother material under actual fire conditions.4)Own measurement according to UL.
Source, GMD, Last Update:04/14/2003
PLEASE CONTACT YOUR LOCAL SALES OFFICE FOR AVAILABILITY IN YOUR AREA DISCLAIMER : THE MATERIALS, PRODUCTS AND SERVICES OF SABIC INNOVATIVE PLASTICS HOLDING BV, ITS
SUBSIDIARIES AND AFFILIATES (\"SELLER\"), ARE SOLD SUBJECT TO SELLER'S STANDARD CONDITIONS OF SALE, WHICH CAN BE FOUND AT http://www.sabic-ip.com.AND ARE AVAILABLE UPON REQUEST.ALTHOUGH ANY INFORMATION OR RECOMMENDATION CONTAINED HEREIN IS GIVEN IN GOOD FAITH, SELLER MAKES NO WARRANTY OR GUARANTEE, EXPRESS OR IMPLIED, (i) THAT THE RESULTSDESCRIBED HEREIN WILL BE OBTAINED UNDER END-USE CONDITIONS, OR (ii) AS TO THE EFFECTIVENESS OR SAFETY OF ANY DESIGN INCORPORATING SELLER'S PRODUCTS,SERVICES OR
RECOMMENDATIONS. EXCEPT AS PROVIDED IN SELLER'S STANDARD CONDITIONS OF SALE, SELLER SHALL NOT BE RESPONSIBLE FOR ANY LOSS RESULTING FROM ANY USE OF ITS PRODUCTS ORSERVICES DESCRIBED HEREIN.Each user is responsible for making its own determination as to the suitability of Seller's products, services or recommendations for the user's particular use through appropriate end-use testingand analysis. Nothing in any document or oral statement shall be deemed to alter or waive any provision of Seller's Standard Conditions of Sale or this Disclaimer,unless it is specifically agreed to in a writing signed Seller. Nostatement Seller concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right of Seller or as a recommendation for theuse of such product, service or design in a manner that infringes any patent or other intellectual property right.* Lexan is a trademark of SABIC Innovative Plastics IP BV© 1997-2008 SABIC Innovative Plastics IP BV.All rights reserved
Lexan* Resin 143R
Americas: COMMERCIAL
PROCESSING PARAMETERS
Injection Molding
Drying TemperatureDrying Time
Drying Time (Cumulative)Maximum Moisture ContentMelt TemperatureNozzle Temperature
Front - Zone 3 TemperatureMiddle - Zone 2 TemperatureRear - Zone 1 TemperatureMold TemperatureBack PressureScrew Speed
Shot to Cylinder SizeVent Depth
1203 - 4480.02
295 - 315290 - 310295 - 315280 - 305215 - 29570 - 950.3 - 0.740 - 7040 - 60
0.025 - 0.076
°Chrshrs%°C°C°C°C°C°CMParpm%mm
TYPICAL VALUEUNIT
• NOTE: Back Pressure, Screw Speed, Shot to Cylinder Size and Vent Depth are only mentioned as general guidelines. These may not apply or needadjustment in specific situations such as low shot sizes, thin wall molding and gas-assist molding.
1)Typical values only. Variations within normal tolerances are possible for variose colours.All values aremeasured at least after 48 hoursstorage at 230C/50% relative humidity.
All properties, expect the melt volume rate are measured on injectionmoulded samples.All samples are prepared according to ISO 294.
2)Only typical data for material selection purpose.Not to be used forpart or tool design.
3)This rating is not intended to reflect hazards presented this or anyother material under actual fire conditions.4)Own measurement according to UL.
Source, GMD, Last Update:04/14/2003
PLEASE CONTACT YOUR LOCAL SALES OFFICE FOR AVAILABILITY IN YOUR AREA DISCLAIMER : THE MATERIALS, PRODUCTS AND SERVICES OF SABIC INNOVATIVE PLASTICS HOLDING BV, ITS
SUBSIDIARIES AND AFFILIATES (\"SELLER\"), ARE SOLD SUBJECT TO SELLER'S STANDARD CONDITIONS OF SALE, WHICH CAN BE FOUND AT http://www.sabic-ip.com.AND ARE AVAILABLE UPON REQUEST.ALTHOUGH ANY INFORMATION OR RECOMMENDATION CONTAINED HEREIN IS GIVEN IN GOOD FAITH, SELLER MAKES NO WARRANTY OR GUARANTEE, EXPRESS OR IMPLIED, (i) THAT THE RESULTSDESCRIBED HEREIN WILL BE OBTAINED UNDER END-USE CONDITIONS, OR (ii) AS TO THE EFFECTIVENESS OR SAFETY OF ANY DESIGN INCORPORATING SELLER'S PRODUCTS,SERVICES OR
RECOMMENDATIONS. EXCEPT AS PROVIDED IN SELLER'S STANDARD CONDITIONS OF SALE, SELLER SHALL NOT BE RESPONSIBLE FOR ANY LOSS RESULTING FROM ANY USE OF ITS PRODUCTS ORSERVICES DESCRIBED HEREIN.Each user is responsible for making its own determination as to the suitability of Seller's products, services or recommendations for the user's particular use through appropriate end-use testingand analysis. Nothing in any document or oral statement shall be deemed to alter or waive any provision of Seller's Standard Conditions of Sale or this Disclaimer,unless it is specifically agreed to in a writing signed Seller. Nostatement Seller concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right of Seller or as a recommendation for theuse of such product, service or design in a manner that infringes any patent or other intellectual property right.* Lexan is a trademark of SABIC Innovative Plastics IP BV© 1997-2008 SABIC Innovative Plastics IP BV.All rights reserved
因篇幅问题不能全部显示,请点此查看更多更全内容
Copyright © 2019- efsc.cn 版权所有 赣ICP备2024042792号-1
违法及侵权请联系:TEL:199 1889 7713 E-MAIL:2724546146@qq.com
本站由北京市万商天勤律师事务所王兴未律师提供法律服务